以萘系(SD)及油系(MP)中间相沥青为原料,对比探究两种沥青制备碳纤维的性能差异。采用扫描电镜、X射线衍射仪、纤维强伸度仪和微欧计等手段表征了碳纤维微观结构及力学与导热性能。结果表明:SD沥青灰分126×10-6,含有约10%的各向同性组分,制得碳纤维拉伸强度1.13GPa,杨氏模量720GPa,热导率790W/(m·K);MP沥青灰分28×10-6,中间相含量100%,制得碳纤维拉伸强度2.21GPa,杨氏模量821GPa,热导率848W/(m·K)。MP碳纤维较SD碳纤维性能更优异的原因在于其具有更大的石墨微晶尺寸、更高的石墨化度及取向度。
The performance differences of the carbon fibers prepared from naphthalene-based (SD) and petroleum-based (MP) mesophase pitch were studied.The microstructures,mechanical properties and thermal conductivity of the carbon fibers were characterized by SEM,XRD,vibrodyn tensile tester and micro ohmmeter.The results shown that the SD pitch had 126ppm ash content and about 10% isotropic components.The tensile strength,Young's modulus and thermal conductivity of the SD carbon fibers were 1.13GPa,720GPa and 790W/(m·K),respectively.The MP pitch had 28ppm ash content and 100% mesophase content.The tensile strength,Young's modulus and thermal conductivity of the MP carbon fibers were 2.21GPa,821GPa and 848W/(m·K),respectively.The reason why the MP carbon fibers had better properties than the SD carbon fibers was that it had larger graphite microcrystalline size,higher graphitization degree and higher orientation degree.
[1] 骆仲泱,王少鹏,方梦祥,等.煤焦油沥青的深度利用及发展前景[J].化工进展,2016,35(2):611-616.
[2] 曲凤娇,刘东,郑凯元,等.中间相沥青的研究进展[J].材料导报,2014,28(1):100-105.
[3] 李崇俊.MPCF增强的C/C复合材料及其在高超音速飞行器的应用[J].高科技纤维与应用,2015,40(3):8-14.
[4] Yuan G,Li X,Dong Z,et al.Pitch-based ribbon-shaped carbon-fiber-reinforced one-dimensional carbon/carbon composites with ultrahigh thermal conductivity[J].Carbon,2014,68(3):413-425.
[5] 史景利,马昌.沥青基碳纤维的研发及产业化[J].高科技纤维与应用,2014,39(3):7-14.
[6] 段春婷,刘均庆,徐文强,等.三种不同原料中间相沥青的性质表征[J].化工进展,2018,37(1):189-194.
[7] Mora E,Blanco C,Santamarí A R,et al.A novel method to obtain a petroleum-derived mesophase pitch suitable as carbon fibre precursor[J].Carbon,2003,41(3):445-452.
[8] 花双平,张博,宋怀河,等.煤沥青基中间相沥青的制备研究[J].炭素技术,2009,28(6):6-10.
[9] 李春霞,徐泽进,乔曼,等.催化裂化油浆超临界萃取组分热缩聚生成中间相沥青的定量研究[J].石油学报(石油加工),2015,31(1):145-152.
[10] 史景利,马昌.纺丝中间相沥青的制备与表征[J].新型炭材料,2019(3):211-219.
[11] Mochida I,Shimizu K,Korai Y,et al.Preparation of mesophase pitch from aromatic hydrocarbons by the aid of HF/BF3[J].Carbon,1990,28(2):311-319.
[12] Mochida I,Yoon S H,Korai Y.Mesoscopic structure and properties of liquid crystalline mesophase pitch and its transformation into carbon fiber[J].Chemical Record,2002,2(2):81-101.
[13] Singer L S.The mesophase and high-modulus carbon fibers from pitch[J].Carbon,1978,16(6):409-415.
[14] 赵稼祥.BP AMOCO公司的碳纤维事业——国外碳纤维进展之二[J].高科技纤维与应用,2000(5):12-17.
[15] 王成扬.碳质中间相理论与应用[M].北京:科学出版社,2015,224-239.
[16] 胡子君.经ZrO2/SO2-4固体超酸催化改性制备中间相沥青[D].太原:中科院山西煤化所,1997.
[17] 马志成.重油的精制及其中间相的稳定性研究[D].长沙:湖南大学,2012.
[18] Qin X,Lu Y,Xiao H,et al.A comparison of the effect of graphitization on microstructures and properties of polyacrylonitrile and mesophase pitch-based carbon fibers[J].Carbon,2012,50(12):4459-4469.
[19] 袁观明.高导热炭材料的制备研究[D].武汉:武汉科技大学,2012.
[20] 叶崇.高导热中间相沥青碳纤维的制备及结构调控[D].长沙:湖南大学,2019.
[21] 刘犇,赵红超,李香粉,等.中间相沥青脱除灰分[J].新型炭材料,2016,31(4):455-458.
基金资助
湖南省知识产权战略推进专项(2019Y024M);湖南创新型省份建设专项经费资助(2019GK2021);湖南省科学技术厅创新创业技术投资项目(2018KG5065);湖南省科技人才专项(2019RS2058)
PDF